LINEA NASTRINI TECNICI RTE
Collezione Ducale
Calzatura
Cotton
Rinforzo e spianatura cuciture
To reinforce and level stitching
COMPOSITION
100% COTTON
THICKNESS
0,33 mm
ELONGATION AT BREAK
1.9 N/Kg
COATING
natural rubber
Bibo
Rinforzo e spianatura cuciture
To reinforce and level stitching
COMPOSITION
65% POLYESTER 35% COTTON
THICKNESS
0,22 mm
ELONGATION AT BREAK
11.7 N/Kg
COATING
natural rubber
Bibo GRS
Rinforzo e spianatura cuciture
To reinforce and level stitching
COMPOSITION
65% POLYESTER GRS 35% COTTON
THICKNESS
0,22 mm
ELONGATION AT BREAK
11.7 N/Kg
COATING
natural rubber
Knit
Maglia altamente qualificata per cuciture su curve difficili
Tape highly recommended for difficult curved-stitching
COMPOSITION
100% POLYESTER
THICKNESS
0,31 mm
ELONGATION AT BREAK
11.8 N/Kg
COATING
natural rubber
Knit Heavy
Rinforzo e spianatura cuciture
Tape for machine use, mainly for leveling of stitching
COMPOSITION
100% POLYESTER
THICKNESS
0,35 mm
ELONGATION AT BREAK
16.5 N/Kg
COATING
natural rubber
Carving
Cotone diagonale ideale per spianatura e cucitura bordi
Diagonal cotton ideal for leveling and stitching edges
COMPOSITION
100% COTTON
THICKNESS
0,28 mm
ELONGATION AT BREAK
4.0 N/Kg
COATING
natural rubber
Nyco SL
Nastro molto sottile ad alta tenacità ideale per colli a “V”
Very light, high tenacity tape, ideal for “V-shapes”
COMPOSITION
65% NYLON – 35% COTTON
THICKNESS
0,34 mm
ELONGATION AT BREAK
103.4
N/Kg
COATING
natural rubber
Nyco MB
Alta resistenza, indicato per tomaia, scollature, cintoli fini
High resistance recommended for uppers, low-cuts and light straps
COMPOSITION
65% NYLON – 35% COTTON
THICKNESS
0,28 mm
ELONGATION AT BREAK
4.0 N/Kg
COATING
natural rubber
Nyco Plus
Articolo simile al Nyco MB ma ancor più compatto e resistente
Similare use of Nyco MB, but more compact and stronger
COMPOSITION
65% NYLON – 35% COTTON
THICKNESS
0,36 mm
ELONGATION AT BREAK
83.5 N/Kg
COATING
natural rubber
Nyco Pes
Rinforzo e spianatura cuciture
To reinforce and level stitching
COMPOSITION
65% NYLON – 35% COTTON
THICKNESS
0,34 mm
ELONGATION AT BREAK
50.6 N/Kg
COATING
acrylic
Mesh
TNT molto fine con rete a rinforzo. Adesivizzabile sul lato non adesivo
Very light non-wowe fabric tape with reinforced mesh. On requiest can be adhesive on both side
COMPOSITION
100% POLIESTER
THICKNESS
0,2 mm
ELONGATION AT BREAK
7.3 N/Kg
COATING
ACRYLIC
Tipar
Lana di vetro. Resistente e rigido, indicato per occhielli e passanti
Glass wool. Resistant and stiff, indicated for eyelets and trough holes
COMPOSITION
100% POLYPROPYLENE
THICKNESS
0,43 mm
ELONGATION AT BREAK
23.6 N/Kg
COATING
hot melt
Lion L
Rinforzo morbido per cintoli e tomaie e per eliminare segno del puntale
Soft reinforcement for straps and uppers and to remove toe caps marks
COMPOSITION
100% POLYESTER
THICKNESS
0.1 mm
ELONGATION AT BREAK
24.2 N/Kg
COATING
natural rubber
Lion L
Rinforzo morbido per cintoli e tomaie e per eliminare segno del puntale
Soft reinforcement for straps and uppers and to remove toe caps marks
COMPOSITION
100% POLYESTER GRS
THICKNESS
0.1 mm
ELONGATION AT BREAK
24.2 N/Kg
COATING
natural rubber
Lion M
Indicato in applicazioni che richiedono maggiore resistenza con stesso grado di morbidezza
Recommended in applicatios which required more resistance e softness at the same time
COMPOSITION
100% POLYESTER
THICKNESS
0,16 mm
ELONGATION AT BREAK
59.3 N/Kg
COATING
natural rubber
Lion L
Rinforzo nei punti difficili per scarpe sportive, tomaie e cintoli
Reinforcement for hard stitches on sport footwear, uppers and straps
COMPOSITION
100% POLYESTER
THICKNESS
0,16 mm
ELONGATION AT BREAK
59.3 N/Kg
COATING
natural rubber
Strong HT
Alta tenacità per tomaia e cintoli
High tenacity for uppers and straps
COMPOSITION
100% NYLON
THICKNESS
0,25 mm
ELONGATION AT BREAK
157 N/Kg
COATING
natural rubber
Hi-Tech
Rinforzo ideale per scarpa sportiva e tecnica
Ideal reinforcement for sport and technical footwear
COMPOSITION
100% POLYESTER
THICKNESS
0,23 mm
ELONGATION AT BREAK
141.8 N/Kg
COATING
natural rubber
Slick
Masking tape bassa temperatura
Low temperature masking tape
COMPOSITION
CELLULOSE
THICKNESS
0,1 mm
ELONGATION AT BREAK
2.5 N/Kg
COATING
acrylic
Slick Plus
Masking tape ad alta temperatura
Hight temperature masking tape
COMPOSITION
CELLULOSE
THICKNESS
0,15 mm
ELONGATION AT BREAK
1.2 N/Kg
COATING
acrylic
Hi-Crunch
Carta crespata. Ideale per curvature
Crepe paper. Ideal for curvatures
COMPOSITION
CELLULOSE
THICKNESS
0,29 mm
ELONGATION AT BREAK
4.7 N/Kg
COATING
acrylic
Designer
Ottimale per modellerie e designer
Ideal for modeling and designers
COMPOSITION
CELLULOSE
THICKNESS
0,15 mm
ELONGATION AT BREAK
2.1 N/Kg
COATING
acrylic
Reverse
Film di solo adesivo, ideale per unire due corpi senza collanti liquidi
Double-adhesive film, ideal for uniting two bodies without liquid adhesives
COMPOSITION
SILICONE PAPER
THICKNESS
0,11 mm
ELONGATION AT BREAK
0.6 N/Kg
COATING
acrylic
Biadesivo
TNT biadesivo strappabile a mano
Non-woven, double-adhesive, tear-away by hand tape
COMPOSITION
CELLULOSE
THICKNESS
0,07 mm
ELONGATION AT BREAK
2.6 N/Kg
COATING
hot melt
Tela Stand
Nastro biadesivo con adesività differenziale. Facilmente removibile senza residui
Double-side tape with different adhesiveness. Easy to remove without leaving residues
COMPOSITION
100% COTTON
THICKNESS
0,3 mm
ELONGATION AT BREAK
11.6 N/Kg
COATING
natural rubber
Propil
Biadesivo in polipropilene resistente allo strappo e removibile
Double-adhesive polypropylene tape, tear-resistant and removable
COMPOSITION
100% POLYPROPYLENE
THICKNESS
0,1 mm
ELONGATION AT BREAK
23.4 N/Kg
COATING
acrylic
Red Tape
Biadesivo ad elevata applicabilità e resistenza ad alte temperature. Ideale per pre-fissaggio chiusure
Double-adhesive tape, highly applicable and resistant to high temperatures. Ideal for pre-fixing latches
COMPOSITION
100% POLYESTER
THICKNESS
0,18 mm
ELONGATION AT BREAK
65.1 N/Kg
COATING
acrylic
Tela Tell
Biadesivo rinforzato con tela di cotone
Double-adhesive tape reinforced with cotton cloth
COMPOSITION
100% COTTON
THICKNESS
0,22 mm
ELONGATION AT BREAK
0.9 N/Kg
COATING
hot melt
Glass Line
Nastro rinforzato con fibra di vetro
Tape reinforced with glass fiber
COMPOSITION
100% POLYESTER
THICKNESS
0,15 mm
ELONGATION AT BREAK
13.9 N/Kg
COATING
acrylic
Glass-Net
Nastro rinforzato con rete in fibra di vetro
Tape reinforced with fiberglass mesh
COMPOSITION
100% POLYESTER
THICKNESS
0,12 mm
ELONGATION AT BREAK
0.9 N/Kg
COATING
acrylic
Reggae
Nastro in plastica autoadesivo. Usato per sorreggere cintoli
Auto-adhesive plastic tape. Used to support straps
COMPOSITION
MIXED PLASTIC MATERIAL
THICKNESS
0,8 mm
ELONGATION AT BREAK
35.4 N/Kg
COATING
hot melt
Iron Paper
Rinforzo adesivo con anima in metallo ideale per cintoli di sandali
Adhesive reinforcement with metal inner. Ideal for sandals straps
COMPOSITION
IRON AND PAPER
THICKNESS
0,8 mm
ELONGATION AT BREAK
8.0 N/Kg
COATING
hot melt
Iron Plastic
Rinforzo adesivo di polietilene ed anima metallica per cintoli dei sandali
Adhesive, polyetylene reinforcement and metal inner for sandals straps
COMPOSITION
IRON AND POLYESTER
THICKNESS
0,11 mm
ELONGATION AT BREAK
26.2 N/Kg
COATING
hot melt
Dispensers
REVERSE
BIADESIVO
Dispenser Elettrico
DISPLAY
3 Dight LED
APPLICABLE TAPE WIDTH
Auto – 20~999 mm
DRIVE
DC motor for tape feed
DC motor for tape cut
DC motor for tape cut
POWER COMPSUNTION
18 watt. With rel of using a big core tape (diameter of reel: 3 inches)
SIZE
137 x 245 x 150 mm
WEIGHT
2,4 kG
COLOR
white